Epoxy Adhesive, DP 420 Series, Dual-Cartridge, 2:1 Mix Ratio, 2 hr Functional Cure
| Item | Epoxy Adhesive |
|---|---|
| Container Type | Dual-Cartridge |
| Functional Cure | 2 hr |
| Mixing Ratio | 2:1 |
| Shear Strength | 4,500 psi |
| Working Time | 20 min |
| Series | DP 420 |
| Consistency | Gel |
| Features | Environmental Resistance, High Peel Strength |
| Primary Application | For General Purpose |
| Maximum Application Temperature | 72 deg F |
| For Use With | Applicator, Mixing Tip |
| Resin Type | Epoxy |
| Compatible Applicator | 3M |
| Total Volume | 200 mL |
| Included Components | Hardener, Resin |
| Compatible Mixer Tip | 3M EPX |
| Minimum Viscosity | 8,000 cps |
| Cure Method | Ambient |
| Non-Sagging | No |
| Materials Bonded | Ceramic, Composites, Concrete, Glass, Metals, Wood, Plastics |
| Maximum Viscosity | 50,000 cps |
| Coverage | 320 sq ft/gal |
| Compatible Primer | Scotch-Weld 3901 Metal Primer |
| Peel Strength | 50 lb/in |
| Hardener Color | Amber |
| Maximum Performance Temperature | 400 deg F |
| Max Visc and Text Consistency | 50,000 cps |
| Compatible Applicator (Grainger Part Number) | 2KVB3 |
| Adhesive Consistency | Liquid |
| Alternate Product Name | Epoxy Adhesive |
| Compatible Mixer Tip (Grainger Part Number) | 2VCY4, 787CR2 |
| Hardness at Full Cure | 77 (85) |
| Hardener Volume | 66.67 mL |
| Includes | none |
| Standards | UL 94 HB |
| Primary Applications | General Purpose |
| VOC Content Weight Percentage | 0% |
| Cured Color | Black |
| VOC Content Weight | 0 g/L |
| Secondary Compatible Materials | Ceramic and Porcelain, Concrete and Masonry, Glass and Fiberglass, Metals, Plastics, Wood |
| Full Cure Time | 24 hr |
| Marine Grade | No |
| Total Vol plus Container Type | 200 mL Dual-Cartridge |
| Color Family | Black |
| Application Method | Two-Part Applicator |
| Tensile Strength | 4,500 psi |
| Low Odor | No |
| Water Resistance | Water-Resistant |
| Interior/Exterior | Exterior, Interior |
| Country of Origin (subject to change) | United States |
| Package Quantity | 1 |