Epoxy Adhesive, DP6310NS Series, Clear, Dual-Cartridge
| Item | Epoxy Adhesive |
|---|---|
| Type | Multi-Purpose |
| Color | Clear |
| Container Type | Dual-Cartridge |
| Materials Bonded | Composite, Glass, Metal, Plastic, Wood |
| Functional Cure | 45 min |
| Standards | No. 49-00093 Revision C, Specification No. CMT0038 |
| Viscosity | 15,000 to 35,000cP |
| VOC Content | 0 |
| Tensile Strength | Not Specified |
| Shear Strength | 50 psi |
| Characteristics | Flexible, Non-Sag Resistance |
| Green Environmental Attribute | Does Not Contain Methylene Chloride |
| Material | Urethane |
| Work Life | 9 min |
| For Use With | Applicator, Mixing Tip |
| Application Family | General Purpose |
| Compatible Applicator | 3M EPX |
| Compatible Primer | EC-3901 for Glass |
| VOC Content Weight Percentage | 0.07% |
| Compatible Applicator (Grainger Part Number) | 794HJ1 |
| Coverage | 320 sq ft/gal |
| Resin Color | Green |
| Total Volume | 400 mL |
| Included Components | Resin and Hardener |
| Cure Method | Ambient |
| Maximum Performance Temperature | 180 deg F |
| Resin Type | Urethane |
| Low Odor | No |
| Water Resistance | Water-Resistant |
| Working Time | 10 min |
| Maximum Application Temperature | 80 deg F |
| Hardener Color | Off-White |
| Compatible Mixer Tip | 7,000,046,633 |
| Non-Sagging | Yes |
| Primary Applications | Composites |
| Application Method | No Special Application |
| Features | Hand-Held Applicator, Humidity Resistant, Primerless to Most Surfaces, Solvent-Free Adhesive System |
| Mixing Ratio | 1:1 |
| Peel Strength | 20 lb/in |
| Alternate Product Name | 3M Scotch-Weld Multi-Material Composite Urethane Adhesive DP6310NS |
| Series | DP6310NS |
| Marine Grade | No |
| Interior/Exterior | Exterior, Interior |
| Cured Color | Green |
| Maximum Viscosity | 35,000 cps |
| Full Cure Time | 24 hr |
| Minimum Viscosity | 12,000 cps |
| VOC Content Weight | Less than 1 g/L |
| Adhesive Consistency | Paste |
| Full Cure | 24 hr |
| Country of Origin (subject to change) | United States |
| Package Quantity | 1 |