Aleación para soldadura fuerte, Proceso Soldadura fuerte, Tipo de aleación Bronce bajo en humos, Contenido de plata 0 Por ciento, Clasificación AWS RBCuZn-C, Diámetro total 1/4 in, Longitud total 36 in, Forma de aleación Varilla, Acabado/Recubrimiento Recubierto de fundente, Sólido 1,590 Grados F, Líquido 1,630 Grados F, Capacidad Tejas 1,750 Grados F, Tamaño de mandril compatible 1,670 Grados F, Serie RBCuZn-C, Tamaño del contenedor 10 lb, Resistencia a la tracción 71 ksi, Límite elástico 64 ksi
| Process | Brazing |
|---|---|
| Standards | AWS A5.8 |
| Length (In.) | 36 |
| Dia. (In.) | 1/4 |
| Brazing Range (F) | 1,670 to 1,750 |
| Container | Box |
| Material | Bronze |
| Application | Brazing |
| Tensile Strength (PSI) | 71,000 |
| Item | Brazing Alloy |
| Package Quantity | 1 |
| Contents | 56% Copper |
| Solidus | 1,590 deg F |
| Tensile Strength | 71 ksi |
| Joining Applications | Cast Iron to Cast Iron, Cast Iron to Copper, Cast Iron to Nickel, Cast Iron to Stainless Steel, Cast Iron to Steel, Copper to Nickel, Copper to Stainless Steel, Copper to Steel, Nickel to Nickel, Nickel to Stainless Steel, Nickel to Steel, Stainless Steel to Stainless Steel, Stainless Steel to Steel, Steel to Steel |
| AWS Classification | RBCuZn-C |
| Elongation | 25% |
| Container Size | 10 lb |
| Capacity Shingles | 1,750 deg F |
| Yield Strength | 64 ksi |
| Finish/Coating | Flux-Coated |
| Overall Length | 36 in |
| Liquidus | 1,630 deg F |
| Flux Application | Flux Not Required |
| Container Type | Box |
| Alloy Form | Rod |
| Series | RBCuZn-C |
| Overall Diameter | 1/4 in |
| Silver Content | 0 % |
| Alloy Composition | 56% to 60% Copper, 0.8% to 1.1% Tin, 0.25% to 1.2% Iron, 0.01% to 0.5% Manganese, 0.05% Lead, 0.04% to 0.15% Silicon, 0.01% Aluminum, 0.5% Other, Balance Zinc |
| Compatible Chuck Size | 1,670 deg F |
| Alloy Type | Low-Fuming Bronze |
| Maximum Brazing Temperature | 1,750 deg F |
| Minimum Brazing Temperature | 1,670 deg F |
| Wire Rope Length | 36 in |
| Length | 36 in |
| Country of Origin (subject to change) | China |